BÖHLER L625 AMPO is a non-magnetic, corrosion and scale-resistant nickel-base alloy. High toughness and strength from the lowest temperatures up to 1000 °C. Good printability.
Particle size distribution 15 – 45 µm:
D10[µm] 18 – 24
D50[µm] 29 – 35
D90[µm] 42 – 50
Apparent density* ≥ 3.5 g/cm³
Measurement of particle size distribution according to ISO 13322-2 (Dynamic image analysis methods);
* Measurement of apparent density is based on ASTM B964 resp. DIN EN ISO 3923-1 and relates to our typical measured values
Achievable mechanical properties of printed part after heat treatment*:
Tensile strength (Rm) 850 ± 50 MPa
Yield strength (RP₀,₂) 550 ± 30 MPa
Elongation (%) 40 ± 5
Hardness 23 ± 5 HRc
*Mechanical strength according to heat treatment AMS5599
Particle size distribution 45 – 90 µm:
Details on request
| SEL | Market grade | UNS | EN |
|---|---|---|---|
| 2.4856 | Alloy 625 | N06625 | NiCr22Mo9Nb |
| C | Cr | Mo | Ni | Co | Ti | Al | Nb | Fe | |
|---|---|---|---|---|---|---|---|---|---|
| 0.05 | 21.50 | 9.00 | ≥ 58.00 | ≤ 1.00 | 0.20 | 0.20 | 3.65 | ≤ 5.00 |